Effect of thermo-mechanical treatments on nano-structure of 9Cr-ODS steel

岡 弘; 丹野 敬嗣; 大塚 智史; 矢野 康英; 上羽 智之; 皆藤 威二; 大沼 正人*

Nuclear Materials and Energy (Internet), 9, p.346 - 352, 2016/12

https://doi.org/10.1016/j.nme.2016.10.007

The effect of thermo-mechanical treatments (TMTs) on the evolution of nano-structure in an oxide dispersion strengthened (ODS) ferritic/martensitic steel (Fe-9Cr-2W-0.22Ti-0.36YO) was investigated. TMTs involve hot extruding and subsequent forging, which are expected to be part of a future industrial-scale manufacturing process of the ODS steel. It was shown that the ODS steel was composed of two phases - a fine-grained residual ferrite phase and a transformable martensite phase. The number density of the nano-sized particles in the residual ferrite phase was significantly higher than that in the martensite phase. The TMTs did not significantly affect the number density, but slightly affected the size distribution of the nano-sized particles in both ferrite phase and martensite phase. Moreover, the volume fraction of the residual ferrite phase decreased after TMTs. In summary, the TMT conditions could be a parameter which affects the nano-structure of the ODS steel.

分散強化型フェライト鋼被覆管製造技術開発(VIIB)

福田 匡*; 阿佐部 和孝*; 池田 浩之*; 山本 祐義*; 松本 一夫*; 福本 博志*; 森本 福男*

PNC TJ9009 96-002, 172 Pages, 1995/10

PNC-TJ9009-96-002.pdf:11.22MB

酸化物分散強化型(ODS)フェライト鋼は耐スエリング性と高温強度に優れることから、大型高速実証炉を対象とした長寿命燃料被覆管材料として注目されている。ODSフェライト鋼の被覆管への適用性を評価するために、本年度は、昨年度に引き続き再結晶組織の導入による強度異方性及び延性・靱性の改善を目的とした検討を実施した。昨年度は、13Cr-3W-0.4Ti-0.25Y2O3(過剰酸素量;0.10wt%)を基本組成とした結果、繰り返し再結晶が不十分でであった。そこで本年度は再結晶がより容易と考えられる成分系13Cr-3W-0.4Ti-0.25Y2O3(過剰酸素量;0.07wt%)を基本組成として選定し、繰り返し再結晶により最終的に再結晶組織を有する被覆管製造条件の検討を行い結果を得た。